Low temperature degradation - ageing of a zirconia dental implant

Mónica Miranda; Tiago Marques; Filipe Araújo; André Correia; Célia Miranda; Maria Helena Fernandes

Low temperature degradation - ageing of a zirconia dental implant

Mónica Miranda, Tiago Marques, Filipe Araújo, André Correia, Célia Miranda, Maria Helena Fernandes

Resultado de pesquisa › revisão de pares

46 Transferências (Pure)

Resumo

This work compares the topographical aspect of the surface and its chemical composition of a zirconia dental implant before and after artificial ageing. Two implants commercialized were analysed, both made from zirconia: Straumann ZLA Pure (TM) Ceramic. The chemical tests performed allowed to identify the elements of the implants' surface and the topographical test was used to observe the surface of the implants before and after ageing. Both tests provide information about the alterations occur on the surface of the implant after ageing.

Idioma original	English
Título da publicação do anfitrião	IRF2016
Subtítulo da publicação do anfitrião	5th International Conference Integrity-Reliability-Failure
Editores	J. F. Silva Gomes, S. A. Meguid
Páginas	895-896
Número de páginas	2
Estado da publicação	Publicado - 2016
Evento	5th International Conference on Integrity-Reliability-Failure - Porto Duração: 24 jul. 2016 → 28 jul. 2016

Conferência

Conferência	5th International Conference on Integrity-Reliability-Failure
País/Território	Portugal
Cidade	Porto
Período	24/07/16 → 28/07/16

Acesso ao documento

37469278Final published version, 4,1 MBLicença: Unspecified

http://hdl.handle.net/10400.14/36467Licença: Unspecified

Citação

@inproceedings{70c8d4973a77400eb5dd9692c98d3671,

title = "Low temperature degradation - ageing of a zirconia dental implant",

abstract = "This work compares the topographical aspect of the surface and its chemical composition of a zirconia dental implant before and after artificial ageing. Two implants commercialized were analysed, both made from zirconia: Straumann ZLA Pure (TM) Ceramic. The chemical tests performed allowed to identify the elements of the implants' surface and the topographical test was used to observe the surface of the implants before and after ageing. Both tests provide information about the alterations occur on the surface of the implant after ageing.",

keywords = "Ceramic, Dental implant, Zirconia, Surface, Ageing",

author = "M{\'o}nica Miranda and Tiago Marques and Filipe Ara{\'u}jo and Andr{\'e} Correia and C{\'e}lia Miranda and Fernandes, {Maria Helena}",

year = "2016",

language = "English",

isbn = "9789899883253",

pages = "895--896",

editor = "Gomes, {J. F. Silva} and Meguid, {S. A.}",

booktitle = "IRF2016",

note = "5th International Conference on Integrity-Reliability-Failure ; Conference date: 24-07-2016 Through 28-07-2016",

}

Miranda, M, Marques, T , Araújo, F , Correia, A, Miranda, C & Fernandes, MH 2016, Low temperature degradation - ageing of a zirconia dental implant. em JFS Gomes & SA Meguid (eds), IRF2016: 5th International Conference Integrity-Reliability-Failure ., 6278, pp. 895-896, 5th International Conference on Integrity-Reliability-Failure, Porto, Portugal, 24/07/16. <http://hdl.handle.net/10400.14/36467>

TY - GEN

T1 - Low temperature degradation - ageing of a zirconia dental implant

AU - Miranda, Mónica

AU - Marques, Tiago

AU - Araújo, Filipe

AU - Correia, André

AU - Miranda, Célia

AU - Fernandes, Maria Helena

PY - 2016

Y1 - 2016

N2 - This work compares the topographical aspect of the surface and its chemical composition of a zirconia dental implant before and after artificial ageing. Two implants commercialized were analysed, both made from zirconia: Straumann ZLA Pure (TM) Ceramic. The chemical tests performed allowed to identify the elements of the implants' surface and the topographical test was used to observe the surface of the implants before and after ageing. Both tests provide information about the alterations occur on the surface of the implant after ageing.

AB - This work compares the topographical aspect of the surface and its chemical composition of a zirconia dental implant before and after artificial ageing. Two implants commercialized were analysed, both made from zirconia: Straumann ZLA Pure (TM) Ceramic. The chemical tests performed allowed to identify the elements of the implants' surface and the topographical test was used to observe the surface of the implants before and after ageing. Both tests provide information about the alterations occur on the surface of the implant after ageing.

KW - Ceramic

KW - Dental implant

KW - Zirconia

KW - Surface

KW - Ageing

M3 - Conference contribution

SN - 9789899883253

SP - 895

EP - 896

BT - IRF2016

A2 - Gomes, J. F. Silva

A2 - Meguid, S. A.

T2 - 5th International Conference on Integrity-Reliability-Failure

Y2 - 24 July 2016 through 28 July 2016

ER -

Low temperature degradation - ageing of a zirconia dental implant

Resumo

Conferência

Acesso ao documento

Impressão digital

Citação